Epoxy moulding compound, inorganically filled, glass fibre reinforced, heat resistant, dimensionally stable, good electric and mechanical properties, very good chemical resistance, low viscosity, UL listed (RTI 155°C)
Encapsulation of electric parts, e.g. electromagnetic coil
Property | Standard | Value | Unit | Test Method |
---|---|---|---|---|
Additional Characteristic | UL, LB, .5, D | |||
Apparent Density | ISO 60 | 0.85 | g/cm³ | |
Ball Indentation Hardness H961/30 | ISO 2039/P1 | 400 | MPa | |
Charpy Impact Strength 23°C | ISO 179-1 eU | 8.5 | kJ/m² | |
Charpy Notched Impact Strength 23°C | ISO 179-1 eA | 4 | kJ/m² | |
Compression - Moulding shrinkage | ISO 2577 | 0.25 | % | |
Compression - Post shrinkage | ISO 2577 | 0.01 | % | |
Compressive Strength Test Specimen Flat Tested | ISO 604 | 250 | MPa | |
Density 23°C | ISO 1183 | 1.89 - 0 | g/cm³ | |
Dissipation Factor 100 Hz | IEC 60250 | 0.02 | ||
Electric Strength 1mm Thickness, Short Term, Electrode Layout P25mm/P25mm in Transformer Oil Equivalent to IEC 60296 | IEC 60243-P1 | 29 | kV/mm | |
Flammability UL 94 | UL 94 | HB / 1.5mm (BK) | Step/mm | |
Flexural Modulus | ISO 178 | 15500 | MPa | |
Flexural Strength 2 mm/min | ISO 178 | 125 | MPa | |
Injection - Moulding Shrinkage | ISO 2577 | 0.3 | % | |
Injection - Post Shrinkage | ISO 2577 | 0.02 | % | |
Proof Tracking Index Test Liquid A | IEC 60112 | 250 | PTI | |
Relative Permittivity 100 Hz | IEC 60250 | 5.5 | ||
Surface Resistivity | IEC 60093 | 1E+12 | Ohm | |
Temp. of Deflection Under Load HDT C-8,0 MPa | ISO 75-2 | 120 | °C | |
Tensile Modulus 1 mm/min | ISO 527 - 1/2 | 13000 | MPa | |
Tensile Strength 5 mm/min | ISO 527 - 1/2 | 55 | MPa | |
Volume Resistivity | IEC 60093 | 1E+13 | Ohm*cm |