Phenolic moulding compound, inorganically filled, glass fibre reinforced, high dimensional stability at raised temperature, good media resistance, heat-resistant
Thermally and dynamically highly stressed parts in automotive field, pulleys
Property | Standard | Value | Unit | Test Method |
---|---|---|---|---|
Additional Characteristic | D | |||
Apparent Density Moulding Compound | ISO 60 | 0.6 | g/cm³ | |
Ball Indentation Hardness H961/30 | ISO 2039/P1 | 400 | MPa | |
Charpy Impact Strength 23°C | ISO 179-1 eU | 12.5 | kJ/m² | |
Charpy Notched Impact Strength 23°C | ISO 179-1 eA | 4.5 | kJ/m² | |
Compression - Moulding shrinkage | ISO 2577 | 0.2 | % | |
Compression - Post shrinkage | ISO 2577 | 0.1 | % | |
Compressive Strength Test Specimen Flat Tested | ISO 604 | 250 | MPa | |
Density 23°C | ISO 1183 | 1.6 | g/cm³ | |
Dissipation Factor 100 Hz | IEC 60250 | 0.1 | ||
Electric Strength 1mm Thickness, Short Term, Electrode Layout P25mm/P25mm in Transformer Oil Equivalent to IEC 60296 | IEC 60243-P1 | 33 | kV/mm | |
Flammability UL 94 | UL 94 | 0 | Step/mm | |
Flexural Modulus | ISO 178 | 12500 | MPa | |
Flexural Strength 2 mm/min | ISO 178 | 175 | MPa | |
Injection - Moulding Shrinkage | ISO 2577 | 0.25 | % | |
Injection - Post Shrinkage | ISO 2577 | 0.1 | % | |
Proof Tracking Index Test Liquid A | IEC 60112 | 0 | PTI | |
Relative Permittivity 100 Hz | IEC 60250 | 6 | ||
Surface Resistivity | IEC 60093 | 1E+10 | Ohm | |
Temp. of Deflection Under Load HDT C-8,0 MPa | ISO 75-2 | 170 | °C | |
Tensile Modulus 1mm/min, Elongatione1 0,05%; e2 0,25% | ISO 527 - 1/2 | MPa | ||
Tensile Strength 5 mm/min | ISO 527 - 1/2 | 0 | MPa | |
Volume Resistivity | IEC 60093 | 1E+11 | Ohm*cm | |
Water Absorption 24h / 23°C | ISO 62 | 14 | mg |